Chemically Crosslinked Polyethylene Foam

Chemically Crosslinked Polyethylene Foam

Chemically crosslinked polyethylene foam. As well as named XLPE foam, XPE foam. It’s produced in continuous rolls resulting in a foam product with uniform, closed cells and smooth skins on both sides. Also light weight, flexible and soft to touch, yet strong, tough, resilient and resistant to moisture, many chemicals and temperature resistant.

It is easy to work in fabricating and thermoforming. XLPE foams are right at home in the building and construction industry with thermal insulation, moisture resistance, sound absorbing and shock absorbing.

Advantages

  • Odorless
  • Lightweight
  • Sound Absorbing
  • Shock Absorbing
  • Moisture Resistant
  • Low Water Absorption
  • Thermal Insulation
  • Easy Fabrication
  • Weather Stability
  • Chemicals Resistant
  • VOC Free
Specification
Thickness Density(kg/m3)
3mm±0.3 300-360 180-220 113-137 90-110 60-74 45-55 36-44 30-36
4mm±0.4 300-360 180-220 113-137 90-110 60-74 45-55 36-44 30-36 25-30.5
5mm±0.4 300-360 180-220 113-137 90-110 60-74 45-55 36-44 30-36 25-30.5
6mm±0.5 300-360 180-220 113-137 90-110 60-74 45-55 36-44 30-36 25-30.5
7mm±0.5 113-137 90-110 60-74 45-55 36-44 30-36 25-30.5
8mm±0.5 113-137 90-110 60-74 45-55 36-44 30-36 25-30.5
9mm±0.5 60-74 45-55 36-44 30-36 25-30.5
10mm±0.7 45-55 36-44 30-36 25-30.5
11mm±0.6 30-36 25-30.5
12mm±0.7 30-36 25-30.5
13mm±0.8 30-36 25-30.5
14mm±0.9 30-36 25-30.5
15mm±1 30-36 25-30.5
Width ≤1m ≤1.5m
Physical Properties
PHYSICAL PROPERTIES Units Test Method Values
Density – Metric Units kg/m3 GB/T 6343-2009 26±3 30±3 35±3 40±5 50±10 65±10 100±10 200±10
Tensile Strength-L Mpa≥ GB/T 6344-2008 0.2 0.25 0.3 0.4 0.48 0.7 0.9 1.6
Tensile Strength-W Mpa≥ GB/T 6344-2008 0.1 0.2 0.24 0.34 0.4 0.5 0.8 1.2
Tear Strength-L Ncm≥ GB/T 1130-2009 8 10 12 16 16 20 30 40
Tear Strength-W Ncm≥ GB/T 1130-2009 6 7 8 14 14 18 25 35
Elongation-L %≥ GB/T 6344-2008 60 80 100 120 130 150 170 190
Elongation-W %≥ GB/T 6344-2008 80 100 110 130 140 160 180 200
Compression Strength 25%Mpa≥ GB/T 8813-2008 0.025 0.03 0.04 0.045 0.05 0.08 0.13 0.17
Thermal Conductivity w∕m•k≤ GB/T 3399-1982 0.036 0.038 0.04 0.04 0.045 0.045 0.045 0.045
Water Absorption %≤ GB/T 8810-2005 8